RBSIC SISIC silicon carbide roller for furnace
Reaction-bonded silicon carbide is the most widely-applied ceramics product. reaction-bonded silicon carbide slip casting process, in combination with the net-size sintering technology and extraordinary finishing capacity, is especiallyapplied toultra-large products with complex shape and tolerance requirements.
Silicon Carbide Ceramics (SiC) belong to non-oxide ceramic, it not only has excellent mechanical properties at room temperature, such as high bending strength, excellent oxidation resistance, good corrosion resistance, high wear resistance and low coefficient of friction, but also the high temperature mechanical properties (strength, creep resistance Etc.) are known to be the best of ceramic materials. Hot pressing sintering, pressureless sintering, hot isostatic pressing sintering of the material, the high temperature strength can be maintained to 1600 ℃, it is the best ceramic material for high temperature strength. Antioxidant properties are also the best of all non-oxide ceramics. Silicon carbide is formed in two ways, reaction bonding and sintering. Each forming method greatly affects the end microstructure. Reaction bonded SIC is made by infiltrating compacts made of mixtures of SiC and carbon with liquid silicon. The silicon reacts with the carbon forming more SiC which bonds the initial SiC particles. Sintered SiC is produced from pure SiC powder with non-oxide sintering aids. Conventional ceramic forming processes are used and the material is sintered in an inert atmosphere at temperatures up to 2000ºC or higher. Both forms of silicon carbide (SiC) are highly wear resistant with good mechanical properties, including high temperature strength and thermal shock resistance. Our engineers are always available to best advise you on the strengths and weaknesses of each ceramic for your particular needs. Silicon Carbide Ceramics Basic Properties: Low density High thermal conductivity (close to aluminium) Good thermal shock resistance Liquid and gas proof High refractoriness(can be used at 1450℃ in air and 1800℃ in neutral atmosphere) It is not affacted by corrosion and do not wet with melted aluminium or melted zinc High hardness Low friction coefficient Abrasion resistance Resists to basic and strong acids Polisheable High mechanical strength Silicon Carbide Ceramics Application: Mechnical components Rotating joints Plain bearings bases pads Pump components Chemical components Mirors Ballistic protection Heat exchanger
Basic Info：
-
Material: Silicon Carbide (SiC RBSIC SSIC)Feature: Long Time MaterialsShape: Pipe Rod
- Color: Grey
- Diameter: 20-200mm
- Usage: Furnace
- Sic: 85-99%
- Advantage: Heat Resistant
- Trademark: Ketao
- Specification: Cusdomized
- Refractoriness (℃): 1580< Refractoriness< 1770
- Type: Heat-Resistant Material
- Max Working Temperature: 1700c
- Length: 200-2000mm
- Delivery Time: 3-20days
- Density: 3.2g/Cm³
- Product Name: Silicon Carbide Beam
- Transport Package: Wooden Case with Foam
- Origin: China
Technical Data:
| Specification data | SISIC/RBSIC | R-SiC | |
| SiC | % | 90~92 | ＞99 |
| Si | % | 8~10 | |
| Density | g/cm3 | >3.02 | 2.65～2.75 |
| Porosity | % | <0.1 | 15-18 |
| Bending strength （20℃） | MPa | 260 | 80～100 |
| Bending strength （1200℃） | MPa | 280 | 90～110 |
| compressive strength （20℃） | MPa | 900 | ≥300 |
| Hardness | Kg/mm2 | 2400 | 1800～2000 |
| Thermal Conductivity （1200℃） | w.m-1.k-1 | 45 | 36 |
| Coefficient of thermal expansion （1200℃） | α×10-6/C | 4.5 | 4.6 |
| Modulus of elasticity （20℃） | GPa | 330 | 280 |
| Maximum operation temperature | ℃ | 1380 | 1650 |
Packaging & Delivery
Packaging Details:
(1) Export safe wooden box
(2)Inner boxes with filler .
(3)Outpackage is high quality cartons .
(4)Custom package
Delivery Time: 30days
Contact me:
Miss Linda Wu
Customer Manager
Tel:+86 0731 23672981
Mobile:+86 13874120538
WeChat ID : hnketao
QQ:2115563697
Skype:linda@hnktgm.com
Email:sales@hnktgm.com
Website: www.hnktgm.com